I.K. Pour, D.J. Krajnovich, et al.
SPIE Optical Materials for High Average Power Lasers 1992
Intermetallic compound (IMC) spalling from electroless Ni-P film was investigated with lead-free solders in terms of solder-deposition methods (electroplating, solder paste, and thin foil), P content in the Ni-P film (4.6, 9, and 13 wt% P), and solder thickness (120 versus .200 μm). The reaction of Ni-P with Sn3.5Ag paste easily led to IMC spalling after 2-min reflow at 250 °C while IMCs adhered to the Ni-P layer after 10-min reflow with electroplated Sn or Sn3.5Ag. It has been shown that not only the solder composition but also the deposition method is important for IMC spalling from the Ni-P layer. The spalling increased with P content as well as with solder volume. Ni3Sn4 intermetallics formed as a needle-shaped morphology at an early stage and changed into a chunk-shape. Needle-shaped compounds exhibited a higher propensity for spalling than chunk-shaped compounds because many channels among the needle-shaped IMCs facilitated Sn penetration. A reaction between the penetrated Sn and the Ni3P layer formed a Ni3SnP layer and Ni3Sn4 IMCs spalled off the Ni3SnP surface. Dewetting of solder from the Ni3SnP layer, however, did not occur even after spalling of most IMCs. © 2004 Materials Research Society.
I.K. Pour, D.J. Krajnovich, et al.
SPIE Optical Materials for High Average Power Lasers 1992
R.D. Murphy, R.O. Watts
Journal of Low Temperature Physics
O.F. Schirmer, W. Berlinger, et al.
Solid State Communications
Min Yang, Jeremy Schaub, et al.
Technical Digest-International Electron Devices Meeting