Some results on the lateral diffusion of indium in thin lead films containing 2.5 wt.% Au are described. At room temperature the diffusion rate is high with a diffusion coefficient D of about 2.5 x 10-12 cm2 s-1 and an activation energy of 0.26±0.1 eV. The indium concentration profile along the films is highly irregular and is characterized by a sharp peak within the diffused film area at the diffusion front. Some of the irregularities are explained by the formation of filaments of near-stoichiometric AuIn2 and by diffusion around grains of varying size. The preferential formation of AuIn2 is likely to be the cause of the lower diffusion rate observed in the Pb-Au films in comparison with pure lead films. It is found that hillocks are nucleated in the vicinity of the indium diffusion front, indicative of strain relaxation. © 1977.
R.W. Gammon, E. Courtens, et al.
Physical Review B
Gregory Czap, Kyungju Noh, et al.
APS Global Physics Summit 2025
Arvind Kumar, Jeffrey J. Welser, et al.
MRS Spring 2000
Thomas H. Baum, Carl E. Larson, et al.
Journal of Organometallic Chemistry